SHANDONG HUITONG STEEL CO.,LTD
| Tipo di pagamento: | T/T,L/C,D/P |
| Incoterm: | FOB,CFR,CIF,EXW |
| Trasporti: | Ocean,Express,Land |
| Porta: | Qingdao,Tianjin,Shanghai |
marchio: H-Tong
Standard: Aisi, Astm, Din, Gb
Place Of Origin: China
Species: Steel Plate
Production Process: Hot Rolled
Application: Boiler Plate, Container Plate, Ship Plate
Special Steel: Wear Resistant Steel, High-Strength Steel Plate
Tolerance: ±1%, ±3%
Category: Cold Rolled Steel Sheet, Boiler Vessel Plate, Low-Alloy Plate, Hot Rolled Steel Sheet, Steel Plate, Ship Steel Plate
Processing Service: Welding, Cutting, Decoiling, Punching, Bending
Surface Treatment: Coated, Clean, blasting and painting according to customer requirement
Thickness: 3-120mm
Width: 600-1500mm, 1800-2000mm,2500-3500mm
Length: 2000-3000mm, 6000-12000mm
| Unità vendibili | : | Ton |
| Tipo pacchetto | : | fascio con striscia d'acciaio |
| Esempio immagine | : |
|
Piastra di usura del carburo di carburo sono fabbricati saldando uno o più strati resistenti all'usura su una piastra di base in acciaio a basso o basso carbonio.
La lega di sovrapposizione ha un'alta quantità di particelle dure in carburo di cromo che fanno sì che la piastra abbia una buona usura e resistenza all'impatto.
Gamma di spessore di sovrapposizione : 3-25 mm
Dimensione della piastra di usura: 1500*3000, 1400*3000.1400*3400, 1400*3500, 2100*3500, personalizzato.
La piastra in acciaio con sovrapposizione in carburo di carburo viene utilizzata per realizzare molte parti di usura complesse da posizionare in luoghi di usura elevati.
Possiamo fornire taglio, flessione, bullone, punzonatura e saldatura di usura secondo i disegni del cliente.
1. La piastra in acciaio resistenti agli indumenti è composta da una piastra in acciaio a basso contenuto di carbonio e uno strato resistente all'usura in lega. Quando si lavora, la matrice fornisce proprietà complete come resistenza, tenacità e plasticità delle forze esterne e lo strato resistente all'usura in lega fornisce proprietà resistenti all'usura che soddisfano i requisiti delle condizioni di lavoro specifiche.
2. Lo strato resistente all'usura in lega in acciaio resistente agli indumenti e la piastra di base sono una combinazione metallurgica. Per mezzo di attrezzature speciali e processi di saldatura automatica, il filo in lega di auto-protezione ad alta resistenza è uniformemente saldato sul substrato e gli strati compositi sono da uno a due o anche di più. Nel processo composito, a causa del diverso rapporto di restringimento della lega, compaiono crepe trasversali uniformi, che è una caratteristica significativa della piastra in acciaio resistente all'usura.
3. Lo strato resistente all'usura della lega è principalmente in lega di cromo, mentre vengono aggiunti manganese, molibdeno, niobio, nichel e altre leghe. La microdurezza del carburo può raggiungere sopra HV1700-2000 e la durezza superficiale può raggiungere HRC58-62. La lega in carburo ha una forte stabilità ad alta temperatura, mantiene un'alta durezza, ma ha anche una buona resistenza all'ossidazione, entro 500 ℃ Uso completamente normale.
4. Lo strato resistente all'usura ha canali stretti (2,5-3,5 mm), canale largo (8-12 mm), curva (s, w), ecc. È composto principalmente da lega di cromo, mentre manganese, molibdeno, niobium, nickel , vengono aggiunti boro e altri componenti in lega. Con un contenuto di carburo del 40-60%, la microdurezza può raggiungere sopra HV1700 e la durezza superficiale può raggiungere HRC58-62.
|
Product |
Wear Resistant Steel Plate |
|
Standard |
AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
|
Thickness |
3-120mm |
|
Width |
600-1500mm, 1800-2000mm,2500-3500mm |
|
Length |
2000-3000mm, 6000-12000mm |
|
Grade |
NM360, NM400, NM450, NM500, AR360, AR400, AR450, AR500, AR550
QUARD400, QUARD450, QUARD500, FORA400, FORA500, RAEX400, RAEX450, RAEX500 |
|
Surface treatment |
Clean, blasting and painting according to customer requirement |
|
Technique |
Cold rolled and hot rolled |
|
Capacity |
10000 tons/month |
|
Package |
Export standard packing: wooden cases or boxes to be packed;We will pack the goods according to the factory's requirements for export. Or according to customer requirements.In addition,we will give the product good surface protection. |
|
Application |
metallurgy, coal, cement, power stntion, mining, building materials, petrochemical industry |
NM360 nm 400 nm 450 nm 500 Piastra in acciaio resistenza all'usura
Componente chimico
|
Steel/Grade |
C |
Si |
Mn |
P |
S |
AL |
Cr+Ni+Mo |
Nb+V+Ti |
|
NM360/AR360 |
0.10-0.30 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<0.6 |
Trace Amount |
|
NM400/AR400 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<0.9 |
|
|
NM450/AR450 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<1.2 |
|
|
NM500/AR500 |
0.10-0.40 |
0.20-0.45 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<1.5 |
|
|
NM550/AR550 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
≤0.015 |
≤0.003 |
≥0.20 |
<2.0 |
|
|
NM600/AR600 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
≤0.015 |
≤0.003 |
≥0.20 |
<2.5 |
Proprietà meccaniche
|
Material |
Tensile MPA |
Elongation% |
Impact energy -20℃ |
HBW |
|
NM300 |
≥1000 |
≥14 |
≥24 |
270-300 |
|
NM360 |
≥1100 |
≥12 |
≥24 |
330-390 |
|
NM400 |
≥1200 |
≥10 |
≥24 |
370-430 |
|
NM450 |
≥1250 |
≥7 |
≥24 |
420-480 |
|
NM500 |
≥1250 |
≥7 |
≥24 |
≥470 |
|
NM550 |
≥1250 |
≥7 |
≥24 |
≥530 |
|
NM600 |
≥1250 |
≥7 |
≥24 |
≥570 |
Mn13 Piastra in acciaio al carbonio ad alto manganese
Composizione chimica (%)
|
Material |
C |
Si |
Mn |
P |
S |
|
Mn13 |
0.90-1.20 |
0.30-0.80 |
11.0-14.0 |
≤0.035 |
≤0.30 |
Proprietà meccaniche
|
Tensile Strength |
Yield Point |
Elongation |
Impact Resistance |
Initial Hardness (HB) |
Hardness after Hardened (HB) |
180° old Bending Test |
|
≥900MPa |
≥295 |
≥40% |
ak≥90J |
200-250 |
≥300 |
Qualified |
Possiamo produrre diverse dimensioni, spessori, larghezze e materiali in base alle tue esigenze
1) Tecnica di produzione
Tagliare grandi piastre in acciaio come requisiti per rendere luminosa la superficie della piastra mediante multile e macinazione, può anche fare fori e fare gradi angolari e può saldare dal disegno.
Per lo spessore inferiore a 30 mm, taglio per laser; Per spessore superiore a 30 mm, principalmente taglio a fuoco oxy.
Per lo spessore della piastra in acciaio da 200 mm, perché durante il taglio della fiamma, la temperatura è molto alta, quindi la piastra di acciaio delle parti di taglio potrebbe essere rotta nella parte angolare, i nostri lavoratori ripareranno gli angoli per essere buone condizioni.
2 ) Applicazione
La piastra in acciaio resistente all'usura con elevata resistenza all'usura e buone prestazioni di impatto sono buone, può essere taglio, flessione, saldatura, ecc. Il processo possiede le caratteristiche del risparmio temporale, conveniente e ampiamente utilizzato in metallurgia, carbone, cemento, centrale elettrica, vetro, minerario, materiali da costruzione, mattoni e industria petrolchimica, rispetto ad altri materiali, ha una performance ad alto costo, è stata favorita da più e più acquirenti.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now