ASTM A335 P5 Tubo in lega in lega hot laminato
Ottieni l'ultimo prezzoTipo di pagamento: | L/C,T/T,D/P,Money Gram,Western Union |
Incoterm: | FOB,CFR,CIF,EXW |
Trasporti: | Ocean,Land,Express |
Porta: | Qingdao,Tianjin,Shanghai |
SHANDONG HUITONG STEEL CO.,LTD
Attività di tipo:Società commerciale , fabbricante
I mercati principali: Africa , Asia , Europa dell'est , Europa , In tutto il mondo
esportatore:51% - 60%
Karts:ISO9001, API, ASME, CE
descrizione:A335 Pipe in acciaio in lega,Tubo in acciaio in lega A335,Tubo in acciaio in lega di carbonio
Tipo di pagamento: | L/C,T/T,D/P,Money Gram,Western Union |
Incoterm: | FOB,CFR,CIF,EXW |
Trasporti: | Ocean,Land,Express |
Porta: | Qingdao,Tianjin,Shanghai |
Modello: ASTM A335 P5
marchio: H-Tong
Standard: bs, GB, ASTM, JIS, DIN, API
Materiale: 10MoWVNb, MO, 10Cr9Mo1VNb, Lega Mn-V, Lega Cr-Mo, 15NiCuMoNb5, 10 # -45 #, Lega CrNi, Q195-Q345
Forma Della Sezione: Il giro
Luogo D'origine: Cina
Applicazione: Tubo del fluido, Tubo della caldaia, Tubo di perforazione, TUBO OLIO, Tubo della struttura, Tubo idraulico, Tubo del gas
Certificazione: Bsi, ce, API
Tubo Speciale: API Pipe, Tubo a parete spessa
Sia Lega: È lega
Tolleranza: ± 1%
Categoria: Tubo in acciaio senza saldatura
Servizio Di Elaborazione: Flessione, Saldatura, Decoiling, Punzonatura, Taglio
Section Shape: Round
Technique: Cold Rolled
Origin: China
HS Code: W005
Outer Diameter: 3 - 80 mm or According to Customer Requirements
Thickness: 0.5-8mm or According to Customer Requirements
Surface: Black Painted,PE Coated,Galvanized,Varnished,HDPE,etc
Surface Treatment: As Per Customer's Request
Grade: 10#, 20#, 45#, 16mn, A213, 35CRMO4, 30CrMo, Q235
Application: Fluid Pipe or Boiler Pipe
Processo Produttivo: Laminati a caldo
Unità vendibili | : | Ton |
Tipo pacchetto | : | Carta anti-acqua e plastica o coperta da lamiera di ferro o legate con tre strisce di reggispi |
Esempio immagine | : | |
Scaricare | : |
Introduzione al prodotto
ASTM A335 s Eamless a lloy s teel p ipe
Il tubo ASTM A335 (ASME S/A335, Chorme-Moly) è un tubo in acciaio in lega ferritica senza soluzione di continuità per un servizio ad alta temperatura. Il tubo ordinato a questa specifica deve essere adatto per flessione, flangia (Vanstoning) e operazioni di formazione simili e per la saldatura di fusione. A volte indicato come "grado P", il tubo cromo Moly è popolare negli gradi P P5, P9, P11, P22 e P91. L'uso più comune dei gradi P11, P22 e P91 è nel settore dell'energia e le piante petro-chimiche, i gradi P5 e P9 sono comunemente utilizzati nelle raffinerie.
A335 è spesso chiamato tubo di moly cromo a causa della composizione chimica di molibdeno (MO) e cromo (CR). Il molibdeno aumenta la resistenza dell'acciaio, nonché il limite elastico, la resistenza all'usura, le qualità di impatto e la intensurabilità. Moly aumenta la resistenza all'ammorbidimento, limita la crescita del grano e rende l'acciaio di cromo meno suscettibile agli abbracci. Moly è il singolo additivo più efficace che aumenta la resistenza allo scorrimento ad alta temperatura. Migliora anche la resistenza alla corrosione dell'acciaio e inibisce la vaiolatura. Il cromo (o il cromo) è il componente essenziale dell'acciaio inossidabile. Qualsiasi acciaio con 12% o più cromo è considerato inossidabile. Il cromo è praticamente insostituibile nel resistere all'ossidazione a temperature elevate. Chrome solleva la trazione, la resa e la durezza a temperature ambiente. Il tubo in acciaio in lega di molibto cromata composizione lo rende ideale per l'uso in centrali elettriche, raffinerie, piante chimiche petrolifere e servizi petroliferi in cui fluidi e gas vengono trasportati a temperature e pressioni estremamente elevate.
S tocks Una gamma completa dei seguenti voti A335:
Specifiche standard per tubi, superheater e tubi di scambiatore di calore ferritico e austenitico senza soluzione di continuità .
Questa specifica copre i tubi di surriscaldamento, superheatro e tubi in acciaio austenitico senza soluzione di continuità. I gradi contenenti la lettera H nella loro designazione hanno requisiti diversi da quelli di gradi simili che non contengono la lettera H. Questi diversi requisiti forniscono una maggiore resistenza alla rottura di scorrimento rispetto a quella normalmente realizzabile in gradi simili senza questi requisiti diversi. I tubi devono essere realizzati con un processo senza soluzione di continuità e devono essere finiti a caldo o a freddo, come specificato. Il grado TP347HFG deve essere finito a freddo. Il trattamento termico deve essere eseguito separatamente e oltre al riscaldamento per la formazione calda. Gli acciai in lega ferritica e inossidabile ferritico devono essere riscaldati. D'altra parte, i tubi in acciaio inossidabile austenitico devono essere arredati in condizioni trattate con calore. In alternativa, immediatamente dopo la formazione calda, mentre la temperatura dei tubi non è inferiore alla temperatura minima della soluzione, i tubi possono essere spenta individualmente in acqua o raffreddato rapidamente con altri mezzi. Il test di tensione, il test di durezza, il test di appiattimento e il test di svasatura devono essere eseguiti su ciascun tubo. Inoltre, ogni provetta deve essere sottoposta al test elettrico non distruttivo o al test idrostatico.
Specifiche di prodotto
Item |
Cold rolled/Hot rolled alloy steel seamless pipe |
|
Standard |
ASTM A209M/ASME 209M, ASME SA210, ASTM A213/ASME SA213M ASTM A333M/ASME SA333/SA333M, ASTM A334M/ASME SA334/SA334M ASTM A335/ASME SA335, ASTM A519, ASTM A691 GB3087, GB6479-2000, GB9948-2006, GB5310-2013, GB5310-95, GB9948-88 DIN 17175, EN10216-2, JISG3467, JISG3458, JIS G3441, NF A49-213/215, BS3059, BS3604, BS3606 |
|
Materials |
A209 T1/SA209 T1, A209 T1b/SA-209 T1b, A209 T1a/SA209 T1a. T2, T5, T9, T11, T12, T22, T23, T24, T91, T911, T92, T122. P1, P2, P5, P5b, P5c, P9, P11, P12, P21, P22, P23, P24, P91, P92. 4118, 4130, 4135, 4137, 4140. 20G, 25MnG, 15MoG, 15CrMoG, 20MoG, 12CrMoG, 12Cr2MoG, 12Cr1MoVG, 12Cr2MoWVTiB, 10Cr9Mo1VNb, 15CrMoG, 10CrMo910. ST35.8, ST45.8, 15Mo3, 13CrMo44, 10CrMo910, 14MoV63,12Cr1MoV. P195GH, P235GH, P265GH, 13CrMo4-5, 10CrMo9-10, 16Mo3, 10CrMo5-5, X10CrMoVNb9-1. GRADE 91, CM65, CM70, CM75, CMSH70, CMS75, CMSH80. GRADE 1/2 Cr, GRADE 1CR, GRADE 1 1/4 CR, 2 1/4 Cr, 3CR, 5CR, 9CR. STPA12, STPA20, STPA22, STPA23, STPA24, STPA25, STPA26. SCR420 TK,SCM415 TK, SCM418 TK, SCM420TK, SCM430TK, SCM435TK, SCM440TK. TU15D3, TU13CD4-04, TU10CD910, TUZ10CD505. S1-622-440, S2-622-440, S1-622-490, S2-622-490, S1-629-470, S2-629-470, S2-629-590. HFS625 CFS625, CFS625. |
|
Description |
Surface |
black painted, PE coated, galvanized |
Length |
5.8m, 6m, 11.8m, 12m, or as required |
|
Wall Thickness |
1-120mm |
|
Outer Diameter |
6-1200mm |
|
Trade terms |
Payment terms |
T/T, L/C, D/P |
Price terms |
FOB, CIF |
|
Package |
Standard export seaworthy package or as required. |
|
Delivery time |
Prompt delivery or as the order quantity. |
|
Export to |
Alloy steel pipe applies to petroleum,chemical industry, electric power, boiler, high temperature resistant, low temperature resistant,corrosion resistant seamless steel pipe used.Alloy steel pipealso can made according to the customer. |
|
Container size |
20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High) 24-26CBM 40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High) 54CBM 40ft HC:12032mm(Length)x2352mm(Width)x2698mm(High) 68CBM |
|
Contact |
If you have any question,please feel free to contact me. |
ASTM A3 3 5 INSEAMENT LEGA ACCIAIO
A335 è spesso chiamato tubo di moly cromo a causa della composizione chimica di molibdeno (MO) e cromo (CR). Il molibdeno aumenta la resistenza dell'acciaio, nonché il limite elastico, la resistenza all'usura, le qualità di impatto e la intensurabilità. Moly aumenta la resistenza all'ammorbidimento, limita la crescita del grano e rende l'acciaio di cromo meno suscettibile agli abbracci. Moly è il singolo additivo più efficace che aumenta la resistenza allo scorrimento ad alta temperatura. Migliora anche la resistenza alla corrosione dell'acciaio e inibisce la vaiolatura. Il cromo (o il cromo) è il componente essenziale dell'acciaio inossidabile. Qualsiasi acciaio con 12% o più cromo è considerato inossidabile. Il cromo è praticamente insostituibile nel resistere all'ossidazione a temperature elevate. Chrome solleva la trazione, la resa e la durezza a temperature ambiente. Il tubo in acciaio in lega di molibto cromata composizione lo rende ideale per l'uso in centrali elettriche, raffinerie, piante chimiche petrolifere e servizi petroliferi in cui fluidi e gas vengono trasportati a temperature e pressioni estremamente elevate.
Composizione chimica:
Grade |
ASTM A335 P5 |
ASTM A335 P9 |
ASTM A335 P11 |
ASTM A335 P12 |
ASTM A335 P22 |
ASTM A335 P91 |
Carbon |
≤0.15 |
≤0.15 |
0.05 – 0.15 |
0.05 – 0.15 |
0.05 – 0.15 |
0.08 – 0.12 |
Manganese |
0.30 – 0.60 |
0.30 – 0.60 |
0.30 – 0.60 |
0.30 – 0.60 |
0.30 – 0.60 |
0.30 – 0.60 |
Phosphorous |
≤0.025 |
≤0.025 |
≤0.025 |
≤0.025 |
≤0.025 |
≤0.020 |
Sulfur |
≤0.025 |
≤0.025 |
≤0.025 |
≤0.025 |
≤0.025 |
≤0.010 |
Silicon |
≤0.50 |
0.25 – 1.00 |
0.50 – 1.00 |
≤0.50 |
≤0.50 |
0.20 -0.50 |
Chromium |
4.00 – 6.00 |
8.00 – 10.00 |
1.00 – 1.50 |
0.80 – 1.25 |
1.90 – 2.60 |
8.00 – 9.50 |
Molybdenum |
0.45 -0.65 |
0.90 – 1.10 |
0.44 – 0.65 |
0.44 – 0.65 |
0.87 – 1.13 |
0.85 – 1.05 |
Proprietà meccaniche:
Tensile Strength, min., psi |
P-5 |
P-9 |
P-11 |
P-22 |
P-91 |
ksi |
60 |
60 |
60 |
60 |
85 |
MPa |
415 |
415 |
415 |
415 |
585 |
Yield Strength, min., psi |
|
|
|
|
|
ksi |
30 |
30 |
30 |
30 |
60 |
MPa |
205 |
205 |
205 |
205 |
415 |
Tensile Strength, min., psi |
P-5 |
P-9 |
P-11 |
P-22 |
P-91 |
P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC]. |
||
|
ksi |
60 |
60 |
60 |
60 |
85 |
||
|
MPa |
415 |
415 |
415 |
415 |
585 |
||
Yield Strength, min., psi |
|
|
|
|
|
|
|
|
|
ksi |
30 |
30 |
30 |
30 |
60 |
|
|
|
MPa |
205 |
205 |
205 |
205 |
415 |
|
|
Esposizione del prodotto
Possiamo produrre diverse dimensioni, spessori, larghezze e materiali in base alle tue esigenze
Test del prodotto
Controlleremo la qualità da parte del tubo in acciaio del materiale, ogni tubo prodotto sarà la propria etichetta Identifica, la qualità controllerà il componente chimico e la proprietà fisica e quindi fornirà il certificato di test materiale. La dimensione delle dimensioni verrà controllata e mostra le immagini al cliente per garantire che tutte le merci soddisfino i requisiti.
Accetta l'ispezione da una terza parte designata/pagata dall'acquirente, come SGS, BV.
Riconosciuto dai clienti in Malesia, Indonesia, Singapore, Filippine, Australia, Perù e Regno Unito. Abbiamo ISO9001/18001, certificati CE.
Chi siamo
Contattaci
Copyright © 2024 SHANDONG HUITONG STEEL CO.,LTDTutti i diritti riservati
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.